Catalytic coating synthesized onto cordierite monolith walls. Its application to diesel soot combustion
Authors: E.D. Banús, V.G. Milt, E.E. Miró, M.A. Ulla
Abstract:
Co,Ba,K/ZrO2 coating onto a cordierite monolith was produced using a sequential process. The first step involved the formation of a ZrO2 layer using a colloidal suspension and the second, the incorporation of active metals. The coating morphology and its physicochemical properties were studied using different characterization techniques. The ZrO2 colloidal suspension and the active ingredients, Co, Ba and K, penetrated through the macropores of the cordierite and their interconnections, both being retained inside the walls and on the external surface. After calcination, the active species were BaCO3, KNO3 and Co3O4.
The catalytic performance for diesel soot combustion was analyzed through the loose deposition of soot onto the structured catalyst and the TPO experiments showed a maximum in combustion rate at about 400 ◦C when NO (0.1%) was added.
Cordierite monoliths are well known as wall-flow type soot filters and the morphology of their walls provides an optimum substrate for the anchoring of a thin catalytic coating, thus achieving an excellent mechanical stability. Moreover, the catalytic layer also covers internal pores of the channel walls, where some ofthe soot particles are trapped, enhancing the catalytic activity and preserving most ofthe original cordierite monolith macroporosity. Therefore, coating cordierite walls with a Co,Ba,K/ZrO2 catalyst constitutes a potential catalytic filter for soot combustion. As the textural properties indicated, no changes in the pore volume were observed after the incorporation ofthe catalytic coating, which favors the potential application of this type of monoliths.
Keywords:
Structured catalyst
Soot combustion
Cordierite monolith
Co,Ba,K/ZrO2 coating
Published in: Applied Catalysis B: Environmental (Volumes 132–133, Pages 1-552, 27 March 2013)
Publisher: Elsevier
ISSN Information: 0926-3373
Catalytic coating synthesized onto cordierite monolith walls. Its application to diesel soot combustion
- Vòng Sơ Khảo Cuộc Thi Đại Sứ Văn Hóa Đọc Năm 2024
- Ngày hội sách “CITTADELLA” khuyến khích và tôn vinh vai trò của sách trong sinh viên Bách khoa
- Cuộc Thi Ảnh “Khoảnh Khắc VNUHCM Libraries”
- Ngày hội Văn hóa đọc lần VI
- Ngày hội văn hóa đọc lần V
- Ngày hội văn hóa đọc lần II
- Ngày hội văn hóa đọc lần IV
- Ngày hội văn hóa đọc lần III
- Tiếp GS Omer Mert Denizci, Trường ĐH Marmara Thổ Nhĩ Kỳ
- Tiếp Cô Claudia Tarzariol Từ The University Of Trento, Italy (Unitrento)
- Tiến sĩ kiều bào Mỹ tặng sách trị giá 150.000 USD cho sinh viên bách khoa
- Khảo sát ý kiến bạn đọc
-
Trực tuyến:18
-
Hôm nay:532
-
Tuần này:21844
-
Tuần trước:29665
-
Tháng trước:48489
-
Tất cả:4103224